Lotrène  Q TR-144 Technical Data Sheet This high molecular weight hexene copolymer is designed for film applications. It has been formulated to provide…. • Good processability • Good toughness and durability • Good blending characteristics with HDPE HMW film resin Typical applicationsinclude: • Multi – wall liners • T-shirt & shopping bags • Trash bags This resin meets these specifications: • FDA Regulation 21CFR 177.1520. Suitab

Minimum order quantity: 5000 Kg

Luban DGDZ-6095 is a high molecular weight, high-density polyethylene copolymer that has been designed specifically for tubular film extrusion. Its broad molecular weight distribution and density successfully combine to give excellent performance at high extrusion rates with high film strength and rigidity. The grade is recommended for high strength grocery sacks, shopping bags and notion and millinery bags. The excellent drawdown characteristic of this product permits production of high- quality thin films for multiwall sack liners and replacements for thin paper products. The combination of strength and drawdown makes this resin ideal for downgauging in many applications. The grade is compatible with color concentrates, thus permitting the production of a variety of colored films that serve as protective and attractive decorative wraps.

Main Characteristics:
• Hexene High Density Resin
• High film strength and stiffness • Excellent drawdown

iAIt
High strength grocery sacks, shopping bags and notion and millinery bags

LUBAN DGDZ HM HDPE

Minimum order quantity: 5000 Kg

Luban 6097
Luban DGDX-6097 is a high molecular weight, high-density polyethylene copolymer that has been designed specifically for tubular film extrusion. Its broad molecular weight distribution and density successfully combine to give excellent performance at high extrusion rates with high film strength and rigidity. The grade is recommended for high strength grocery sacks, shopping bags and notion and millinery bags. The excellent drawdown characteristic of this product permits production of highquality thin films for multi-wall sack liners and replacement for thin paper products. The combination of strength and drawdown makes this resin ideal for downgauging in many applications. The grade is compatible with color concentrates, thus permitting the production of a variety of colored films that serve as protective and attractive decorative wraps. Main Characteristics: • Butene High Density Resin • High film strength • Excellent drawdown

Application ion High strength grocery sacks, shopping bags and notion and millinery bags Properties (Typical Values) operties (Typical Values) Property Unit Test method Value* Melt Index (190°C/2.16 kg) g/10 min ASTM D1238 0.05 Melt Index (190°C/21.6 kg) g/10 min ASTM D1238 9 Density g /cm³ ASTM D792 0.948 Flexural Modulus - 1% Secant MPa ASTM D790* 1040 Tensile stress at yield (MD/TD) MPa ASTM D638* 30/27 Tensile stress at break (MD/TD) MPa ASTM D638* 51/60 Tensile strain at break (MD/TD) % ASTM D638* 220/400 Dart Drop Impact (12.7 μm) g ASTM 1709A* 127 Vicat Softening Temperature °C ASTM D1525 123 Melting Temperature (DSC) °C ASTM D3418 129

Minimum order quantity: 5000 Kg

This high molecular weight, hexene copolymer is tailoredfor blown film applications that require: Toughness and durability Good processability Good blending characteristics with HDPE HMWresinsTypical applications for HHM TR-144 include: T-shirt bags Multi-wall liners Trash bags

Nominal Resin Properties(1,2) Value (SI Units) Method Density 0.946 g/cm3 ASTM D1505 Melt Index, Condition 190°C / 2.16 kg 0.18 g/10 min ASTM D1238 Brittleness Temperature, Type A clamp, Type I specimen <-75°C ASTM D746 ESCR, Condition B (100% Igepal), F50 >1000 hrs ASTM D1693 Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min 1150 MPa ASTM D790 Nominal Blown Film Properties at 0.025mm (1,3) Value (SI Units) Method Dart Drop (66 cm) 90 g ASTM D1709 Tensile Strength at Yield, 50.8 mm/min MD 24 MPa ASTM D882 Tensile Strength at Yield, 50.8 mm/min TD 26 MPa ASTM D882 Elongation at Break, 50.8 mm/min MD 480% ASTM D882 Elongation at Break, 50.8 mm/min TD 640% ASTM D882 Elmendorf Tear Strength, MD 19 g ASTM D1922 Elmendorf Tear Strength, TD 270 g ASTM D1922 1. The nominal properties reported herein are typical of the product, but do not reflect normal testing variance and therefore should

Minimum order quantity: 5000 Kg

HMELPolysure B0155D is a 1-Hexene co-monomer based High Density Polyethylene, produced by Advanced Dual Loop Slurry MarTECHTM technology, suitable for Blow Molding process. B0155D offers exceptional processability, very good melt strength, excellent die swell properties.

Minimum order quantity: 5000 Kg

FJ00952 is a TNPP additive free, high molecular weight high density polyethylene copolymer grade specifically designed for blown film applications. Its high molecular weight, broad molecular weight distribution and high density combine successfully to give excellent extrudability with high film strength and rigidity.

Typical Applications: FJ00952 resin is recommended for blown film extrusion. this product is suggested for the manufacture of high strength grocery sacks, shopping bags and high quality thin films for multi wall sack liners and replacement for thin paper products. Films of this product can be readily treated and printed to give high quality graphics.Information provided by SABIC.

Minimum order quantity: 5000 Kg

F5400 is a film grade HM-HDPE produced by the Mitsui CX Technology F5400 can be used for general-purpose Films as well as very thin Reinforced bags F5400 grade is characterized by excellent processability and high mechanical strength

Minimum order quantity: 5000 Kg

Qamar F1  is a high molecular weight high density polyethylene blow moulding grade combining blow moulding extrusion behavior and superior mechanical properties. Blow moulded items made from HB 0035 exhibit high impact strength and good stress cracking resistance and high stiffness. HB 0035 contains antioxidant to protect the polymer from degradation during processing. HB 0035 is a highly crystalline, non-polar thermoplastic and has excellent chemical resistance and superb impact resistance at ambient conditions and even at cold temperatures. Applications: HB0035 is well suited for wide range of blow moulding applications due to its unique properties. These range from bottles for bleach, motor oil, toiletries, mild and distilled water. This grade is also used to make small containers (from 10 cc to 20 lit.). 

Minimum order quantity: 5000 Kg

VistamaxxTM Performance Polymer 6102

Propylene Elastomer

Suitable for a wide range of film and compounding applications.

• Other typical applications include calendered or extruded profiles, foamed or blown molded goods and thermoformed products.
• Excellent adhesion to conventional or metallocene PP and PE.

• Very good elasticity, toughness and melt strength.

• Very low seal initiation temperature combined with high seal strength when used as sealing layer of co-extruded structures.

• Very good chemical resistance and long term aging. • RoHS compliant.

Minimum order quantity: 5000 Kg

EL-LENE H5604F is a product of bi-modal process from Mitsui Chemicals, Inc. of Japan.

Typical Applications

• Recommend film thickness at 10-25 micron

• Shopping bag and T-shirt bag

• Garbage bag

• Liner bag

Product Characteristics

Physical properties

Property

Resin Properties

Melt Flow Rate
Density
Melting Point
Vicat Softening Point Brittleness Temperature ESCR

Film Properties

Tensile Strength at Yield Tensile Strength at Break Tensile Modulus, 2% Secant Elongation at Break Elmendorf Tear Strength Dart Impact Strength

Test Method

High tensile strength with good dart impact strength High stiffness

Low gel content
Good moisture barrier

Food contact applicable (Complies with U.S FDA 21 CFR 177.1520)

Minimum order quantity: 5000 Kg

ExxonMobil™ HD 7960.13 is a high molecular weight high density polyethylene blown film resin. Films made from HD 7960.13 resin exhibit excellent impact and toughness properties, as well as high stiffness. HD 7960.13 resin is particularly recommended for films less than 0.5 mil in thickness.

Minimum order quantity: 5000 Kg

HB0035 is a high molecular weight high density polyethylene blow moulding grade combining blow moulding extrusion behavior and superior mechanical properties. Blow moulded items made from HB 0035 exhibit high impact strength and good stress cracking resistance and high stiffness. HB 0035 contains antioxidant to protect the polymer from degradation during processing. HB 0035 is a highly crystalline, non-polar thermoplastic and has excellent chemical resistance and superb impact resistance at ambient conditions and even at cold temperatures.
Applications: HB0035 is well suited for wide range of blow moulding applications due to its unique properties. These range from bottles for bleach, motor oil, toiletries, mild and distilled water. This grade is also used to make small containers (from 10 cc to 20 lit.).

Minimum order quantity: 5000 Kg

HTA 001HP5 is a high molecular weight HDPE film grade providing very good processability on high output extruders. Films made from HTA 001HP5 exhibit excellent impact and toughness properties as well as high stiffness.

Minimum order quantity: 5000 Kg

Oriented Tape & Monofilament

High Density Polyethylene

012E50 is a High Density Polyethylene manufactured using Nova Chemical's Sclairtech Solution Polymerisation Technology with following features:

Excellent processability

Superior mechanical properties

Lower water carryover

HDPE 012E50 is recommended for following applications

Tarpaulin

woven sacks

Monofilaments for mosquito nets , fishing nets & filter cloth etc 

Minimum order quantity: 5000 Kg

Aramco HDPE F5101 is a high molecular weight high density polyethylene resin and is typically used in for blown film process especially for thin film applications. This resin has broad molecular weight distribution that makes it easier to process. Films made from this resin typically exhibits high stiffness with excellent impact and toughness characteristics. Typical Applications Shopping bags, trash bags, industrial liners. This product is not intended for use in medical and pharmaceutical applications.

Minimum order quantity: 5000 Kg

SABIC® HDPE B5429 High density polyethylene for Blow moulding

Description. SABIC® HDPE B5429 is a medium molecular weight high density polyethylene copolymer. It is primarily intended for blow moulding bottles of small sizes. SABIC® HDPE B5429 offers an excellent combination of toughness, stress cracking resistance (ESCR), load bearing strength and processability characteristics.

Typical applications. SABIC® HDPE B5429 is classified as a multipurpose blow moulding grade. It may be blow moulded into containers for household and industrial chemicals (e.g. detergents, bleach, fabric softeners, solvents, paints, etc.), automotive supplies, foodstuffs, toiletries and cosmetics. It can also be used in other hollow thin-walled parts and profile extrusions.

Processing conditions. SABIC® HDPE B5429 has been run on the latest high speed blow moulding machines at maximum rates to produce articles of excellent quality. Moulded parts exhibit outstanding surface appearance. The recommended melt temperature for this grade is between 165 and 215 °C.

Minimum order quantity: 5000 Kg

P4808 is a natural bimodal high density polyethylene (HDPE) resin, specifically designed for non-pressure pipe extrusion application. It provides good stress crack resistance properties (ESCR).

Minimum order quantity: 5000 Kg

8003 are an ethylene/butene copolymer. The trade name is TAISOX. This product manufactured by the CSTR slurry process. It provides high stiffness, good impact and processing , good chemical resistance.
8003 is suitable for packaging bottle,dairy bottle, medicine cans,Tool box.

Processability

TAISOX 8003 HDPE Resin can be extruded at temperature profiles between 150 and 180°C

Minimum order quantity: 5000 Kg

B5004
High Density Polyethylene Blow Molding

Product Description: HDPE B5004 is a natural colored grade produced with the latest Mitsui CX slurry polymerization Technology exhibiting following features: ¸
Good Processing Properties ¸
Excellent ESCR Properties ¸
Good external appearance

HDPE B5004 is recommended for following applications: ¸
Bottles & containers up to 10 L ¸
Packaging of Pesticides & Surfactants ¸
Bottles for Shampoo and Cosme

Minimum order quantity: 5000 Kg

F52H04
High Density Polyethylene Film Extrusion

Product Description: HDPE F52H04 is a natural colored grade produced with the latest Mitsui CX slurry polymerization Technology exhibiting following features:
 Excellent Mechanical Strength
 High Stiffness
 Excellent processability (at High Speed)

HDPE F52H04 is recommended for following applications:
 Tissue-like films
 Garment/Grocery/merchandise bags
 Disposal waste bags
 Shopping/Counter bags 

Minimum order quantity: 5000 Kg

B55F003

High Density Polyethylene Blow Molding

Product Description: HDPE B55H03 is a natural colored grade produced with the latest Mitsui CX slurry polymerization Technology exhibiting following features:
High Impact Strength
 Rigidity
 Low Parison Sag
 Good ESCR Properties

HDPE B55H03 is recommended for following applications:
 Large Containers (up to 100L) for transport & storage of Chemicals, Detergent, Lube Oil etc.
 Blow Molded Water Tanks (up to 1000L)

Minimum order quantity: 5000 Kg

M6008 Opal HDPE Injection moulding granules

High Density Polyethylene Injection Molding

Product Description: HDPE M6008 is a natural colored grade produced with the latest Ineos Gas Phase polymerization Technology exhibiting following features:
 Excellent Mechanical Properties
 Very Good processability
 Good dimensional stability
 Good aesthetics of finished products

HDPE M6008 is recommended for following applications:
 Material handling crates
 Helmets
 Caps & Closures
 Luggage shells

Minimum order quantity: 5000 Kg

R5410 HDPE Granules Opal Raffia 0.9MFI

High Density Polyethylene Raffia & Monofilament

Product Description: HDPE R5410 is a natural colored grade produced with the latest Ineos Gas Phase polymerization Technology exhibiting following features:
 Exceptional Tenacity
 Excellent processability

HDPE R5410 is recommended for following applications:
 Woven Sacks & Tarpaulin
 Knitted nets for crop protection
 “ Raschel’’ sacks for vegetables
 Ropes

Minimum order quantity: 5000 Kg

Relene B5502 is a High-Density Polyethylene grade for general purpose extrusion blow molding applications. It also offers excellent melt strength, very good swell characteristics and easy processability. Articles processed from this grade exhibit excellent balance of stiffness, impact strength. This grade can be used for general-purpose applications.

Typical Characteristics• Property Test Method Unit Typical Value••
Melt Flow Index (190°C/5.0 kg) ASTM D1238 gm/10 min 1.4 Density (23ºC) ASTM D 1505 gm/cm3 0.955 Tensile Strength at Yield ASTM D638 MPa 26 Elongation atYield ASTM D638 % 11 Elongation atBreak ASTM D638 % 750 Flexural Modulus ASTM D790 MPa 1100 Vicat Softening Point ASTM D1525 ºC 128 *Typical Characteristics and notto betaken asspecifications

**Mechanical Properties are on Compression molded specimen Applications:
 General purpose blow molded containers, jerry cans up to 15 liters. Regulatory Information:
 For regulatory information please contact organization representative. Storage Recommendations:
 Bags should be stored in dry/closed conditions at temperatures below 50°C and protected from UV / direct sunlight.

Minimum order quantity: 5000 Kg

F46003 HIGH DENSITY POLYETHYLENE BLOW MOULDING & BLOWN FILM GRADE

F46003 is a High Density Polyethylene grade suitable for general purpose blown film & extrusion blow moulding applications. Articles blown fromthis grade exhibit moderate to good stiffness. The resin offers good melt strength, ESCR and impact resistance. TYPICAL CHARACTERISTICS* PROPERTY TEST METHOD UNIT TYPICAL VALUE Density (23 oC) ASTM D 1505 g/cc 0.946 Melt Flow Index (190 oC / 2.16 Kg) ASTM D 1238 g/10 min. 0.38 Film Properties** Tensile Strength at Yield (MD / TD) ASTM D 882 MPa 29.0/26.0 Ultimate Tensile Strength (MD / TD) ASTM D 882 MPa 45.0/40.0 Elongation at Break (MD / TD) ASTM D 882 % 780 /950 Dart Impact Strength, F50 (38 mm dart, 66 cm height) ASTM D 1709 g/ mic. 1.8 Tear Strength (MD / TD) ASTM D 1922 g/µm 0.4 /4.5 * Typical characteristics and not to be taken as specifications **

Typical properties measured on 40 µm film made with 0.8 mm die gap & 2.7 BUR

APPLICATIONS: Used for producing blown film and is recommended for use in carry bags and co-extruded film structures, general purpose blow molded containers.

Minimum order quantity: 5000 Kg

53EA010 HDPE Granules Reliance Raffia grade for stretched tape products. 

Applications - Oriented Tapes, Woven sacks


Density - 0.955

1mfi

Minimum order quantity: 5000 Kg

M60075 is a High Density Polyethylene (HDPE) grade suitable for injection moulding applications where good mechanical properties are essential with gloss, dimensional stability, good ESCR, required for technical mouldings like moulded crates, luggage shells, helmets, defence applications, etc.

Typical Characteristics Property Test Method Unit Typical Value** Density (23°C) ASTM D1505 g/cc 0.960 MFI (190°C/2.16 kg) ASTM D1238 g/10 min 8.0 Tensile Strength at Yield ASTM D638 MPa 25 Elongation at Break ASTM D638 % 800 Flexural Yield Strength ASTM D790 MPa 30 Flexural Modulus ASTM D790 MPa 900 Hardness ASTM D2240 Shore D 69 0 Vicat Softening Point ASTM D1525 C 128 Izod Impact Strength ASTM D256 J/m 88

Applications - Crates, Luggage and Industrial containers.

Minimum order quantity: 5000 Kg

High Density Polyethylene Technical Data Sheet (TDS) - Provisional

UF5205H

Product Description:

Blown Film

TDS-PE-103-UF5205H (Provisional)

Asrene® UF5205H is a monomodal HDPE resin which is supplied in natural pellet form and suitable for blown film, shopping bags, grocery and seed bags, disposal bags, and industrial liners application which require good film impact and good tear strength characteristic.

Product Characteristics:

 Hexene copolymer  Good film impact
 Good tear strength

Vicat Softening Temperature

Applications:

 Blown film
 Shopping bags
 Grocery and seed bags  Disposal bags
 Industrial liners

Minimum order quantity: 5000 Kg

High Density Polyethylene Technical Data Sheet (TDS)

UB5206H

Product Description:

Blow Molding

TDS-PE-100-UB5206H-03

Asrene® UB5206H is an HDPE resin which is supplied in natural pellet form and suitable for blow molding, drum and industrial parts, large-sized containers, synthetic rattan, water tank, as well as for non-pressure pipes requiring excellent impact resistance, ESCR, and rigidity.

Product Characteristics:

 Hexene copolymer
 Excellent impact resistance  Excellent ESCR
 Excellent rigidity

Vicat Softening Temperature

Applications:

 Blow molding
 Large-sized containers (up to 150L)  Water tank
 Drum and industrial parts
 Non-pressure pipes
 Synthetic Rattan

ASTM D 1525

oC

125

Minimum order quantity: 5000 Kg

F0050D Polysure HDPE HM Film

Product Characteristics:

Polysure F0050D is a 1-Hexene co-monomer based Bimodal High Molecular Weight High Density Polyethylene, produced by Advanced Dual Loop Slurry MarTECHTM technology, suitable for Blown Film Extrusion process. F0050D resin comes with a combination of excellent processability, good bubble stability, superb mechanical properties. Films produced with F0050D boasts of excellent toughness and durability.

Recommended Applications:

Heavy duty films for Industrial liners, Merchandise bags, Trash bags, General purpose shopping bags, Carry bag for grocery, Food packaging

Typical Properties:

Resin Properties

1. 1  Melt Flow Index (190°C & 2.16 kg)

2. 2  Melt Flow Index (190oC & 21.6 kg)

3. 3  Density (23°C)

Film Properties*

1. 1  Tensile Strength at Yield (MD/TD)

2. 2  Tensile Strength at Break (MD/TD)

3. 3  Tensile Elongation at Break (MD/TD)

4. 4  Elmendorf Tear Strength (MD/TD)

5. 5  Dart Impact Strength

ASTM D1238 ASTM D1505

ASTM D882 (50 mm / min)

ASTM D1922 ASTM D1709A

g/10 min g/10 min g/cc

MPa MPa % g/micron g/micron

0.05 8 0.950

30 / 32

95 / 47 200 / 520 0.8 / 20 8.7

*The film properties have been measured on 20 μm thick films (Blow-up ratio: 4, Die Gap: 1 mm))

Minimum order quantity: 5000 Kg

HF0961 is a pelleted high molecular weight, high density polyethylene Hexene-1 resin for tubular film extrusion. HF0961 meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 3.1a & 3.2a.

Grocery sacks, shopping bags, liners notion and millinery bag

High extrusion rate with high film strength and rigidity, excellent draw down for high quality thin film.

Minimum order quantity: 5000 Kg

POLYETHYLENE Borstar® HE1440 ENHANCED POLYETHYLENE FOR HIGH PERFORMANCE AGRICULTURE PIPE APPLICATIONS DESCRIPTION Borstar®HE1490 is a Black, bimodal HDPE product produced using the proprietary Borstar® bimodal technology which offers excellent melt strength and process ability for sprinkler pipe extrusion and drip lateral with superior mechanical properties. CAS-No. 25087-34-7 APPLICATIONS HE1440 is recommended for:  Range of wall thickness for drip irrigation tubing for online drip lateral and flat as well as cylindrical emitting pipe/inline production  Sprinkler Irrigation pipes  Non pressure utility pipes KEY FEATURES HE1440 offers excellent balance of process-ability and mechanical properties

PHYSICAL PROPERITES Property Typical Value* Test Method Density 954 kg/m3 ASTM D 792 Melt Flow Rate (190°C/5.0kg) 0.50 g/10min ASTM D1238 Tensile Modulus (1 mm/min) >800 MPa ISO 527-2 Tensile Strain at Break (50 mm/min) >600% ISO 527-2 Tensile Stress at Yield ( 50 mm/min) 20 MPa ISO 527 -2 Melting Temperature 128 °C ISO 11357/03 * Typical properties and data should not be used for specification work 

Minimum order quantity: 5000 Kg

P0049D Polysure HDPE PE 100 Pipe

Product Characteristics:

Polysure P0049D is a 1-Hexene co-monomer based Bimodal high molecular weight High Density Polyethylene, produced by Advanced Dual Loop Slurry MarTECHTM technology, suitable for Pipe Extrusion process. P0049D offers excellent processability, good toughness & outstanding creep resistance. Pipes made with P0049D have smooth surface finish, superb mechanical properties including long term hoop strength, resistance to slow crack growth and rapid crack propagation. Pipes when produced with P0049D and optimum dosage of carbon black as specified in clause 5.2.3 of IS 4984, will meet the hydrostatic strength requirement of PE 100 class of pipes.

Recommended Applications:

PE 100 pressure pipes used in Potable water distribution, Gas distribution pipes, High performance industrial pipes.

Typical Properties:

Resin Properties

1. 1  Melt Flow Index (190°C & 5 kg)

2. 2  Melt Flow Index (190°C & 21.6 kg)

3. 3  Density (23°C)

4. 4  Tensile Strength at Yield, Type IV Specimen

5. 5  Tensile Elongation at Break, Type IV Specimen

6. 6  Flexural Modulus (1% Secant)

7. 7  Notched Izod Impact Strength (23°C)

8. 8  Vicat Softening Point (10N)

9. 9  ESCR (F50), 10% Igepal

10. 10  Oxidative Induction Time

Pipe Properties#

1. 1  Slow Crack Growth Test

2. 2  Minimum Required Strength

3. 3  Hydrostatic Pressure Test at Induced Stress 5.7 MPa

4. 4  Hydrostatic Pressure Test at Induced Stress 5.5 MPa

ASTM D1238

ASTM D1505

ASTM D638 (50 mm / min)

ASTM D790A ASTM D256A ASTM D1525 ASTM D1693B ASTM D3895

ISO 13479 ISO 9080

IS 4984

g/10 min 0.26 g/10 min 8

g/cc 0.949 MPa 26

% >700 MPa 1000

J/m 280 °C 125

Hour
min >30

Hour >500 MPa 10 Hour ≥48

>1000

(80°C) Hour ≥165

Minimum order quantity: 5000 Kg

Hostalen CRP 100 black

Polyethylene, High Density

Product Description

Hostalen CRP 100 black is a high density polyethylene (HDPE), black coloured similar RAL 9004 with high melt viscosity for extrusion, injection and compression moulding. The product is classified as PE 100 and provides excellent stress crack resistance properties (ESCR) combined with very good long term hydrostatic strength.

It is not intended for medical and pharmaceutical applications.

Product Characteristics Status

Test Method used
Availability
Processing Method
Typical Customer Applications

Typical Properties Physical
Density
Melt flow rate (MFR)

(190°C/21.6kg)

(190°C/5.0kg)

Mechanical

Tensile Modulus (23 °C, v = 1 mm/min, Secant) Tensile Stress at Yield (23 °C, v = 50 mm/min) Tensile Strain at Yield (23 °C, v = 50 mm/min) Tensile Creep Modulus 1h

Note: [Test stress in MPa] Tensile Creep Modulus 1000h Note: [Test stress in MPa]

Maximum elongation TD

MRS classification
FNCT (4.0 MPa, 2% Arkopal N 100, 80°C) Flexural creep modulus

(4 point loading method, 1 min-value) (4 point loading method, 24 h-value) (4 point loading method, 2000 h-value)

Commercial: Active

ISO

Europe, Asia-Pacific

Extrusion Pipe Sheet and Semi Finished Products

Gas Pipe, Industrial, Soil & Waste Pipe, Drinking Water Pipe

Method

ISO 1183 ISO 1133

ISO 527-1, -2 ISO 527-1, -2 ISO 527-1, -2 ISO 899-1

ISO 899-1 EN 638

ISO/TR 9080 ISO 16770 DIN 19537-2

Value

0.959

6.4 0.23

900
23
8
850 [2.0]

360 [2.0]

> 350 > 350 10
> 1000

1100 560 330

Unit

g/cm3

g/10 min g/10 min

MPa MPa % MPa

MPa

% % MPa h

MPa MPa MPa

Minimum order quantity: 5000 Kg

SABIC® HDPE PIPE

P6006

PRODUCT DESCRIPTION

P6006 is black compound high density (class MRS 10 - PE 100) Polyethylene with bimodal distribution of molecular mass. It is

specifically designed for pressure Pipe applications. It provides excellent stress crack resistance properties (ESCR) combined

with very good long term hydrostatic strength.

TYPICAL APPLICATIONS

P6006 Pressure pipes for drinking water, irrigation, gas distribution and waste water pipes. It is also recommended for

manufacture of chemical liners and containers.

TYPICAL DATA

(1) Typical values: not to be construed as specification limits.

(2) Properties are based on 20 m film produced at4 BUR using 100% P6006.

(3) Test specimen according to ISO 527-2 type 1 BA, thickness 2mm with 50mm/min test speed.

Processing Conditions:

Typical processing conditions for P6006

Melt temperature: 190-220°C

PROPERTIES Unit Value (1) Test Method

Melt Flow Rate

@ 190°C & 5 kg load g/10 min 0.23 ISO 1133

@ 190°C & 21.6 kg load 6.2

Carbon Black content % 2.25 ISO 6964

Density @ 23°C Kg/m3 959 ISO 1183

MECHANICAL PROPERTIES(2)

Tensile Strength @ Yield(3) MPa 23 ISO 527-2

Tensile Elongation @ Yield(3) % 9

Tensile Modulus(3) MPa 900

Charpy Impact Notched

@ 23°C kJ/m2 26 ISO 179

@ -30°C 13

Hardness (Shore D) - 63 ISO 868

THERMAL PROPERTIES

Vicat Softening Point @ 50N (VST/B) °C 74 ISO 306

OIT (210°C) Min > 20 EN 728

Minimum order quantity: 5000 Kg

Minimum order quantity: 5000 Kg

R0150S Polysure HDPE Raffia

Product Characteristics:

Polysure R0150S is 1-butene comonomer based High Density Polyethylene, produced by Gas Phase – UNIPOLTM PE technology, suitable for Raffia tape Extrusion process. R0150S resin offers excellent processability with low water carry over, good stretchability, superior mechanicals, and resistance to fibrillation.

Recommended Applications:

Woven sacks, Raffia, Tarpaulins

Typical Properties:

1. 1  Melt Flow Index (190°C & 2.16 kg)

2. 2  Density (23°C)

3. 3  Tensile Strength at Yield, Type IV Specimen

4. 4  Tensile Strength at Break, Type IV Specimen

5. 5  Tensile Elongation at Break, Type IV Specimen

6. 6  Flexural Modulus (1% Secant)

7. 7  Notched Izod Impact Strength (23°C)

8. 8  Vicat Softening Point (10N)

ASTM D1238 ASTM D1505

ASTM D638 (50 mm / min)

ASTM D790A ASTM D256 ASTM D1525

g/10 min 1 g/cc 0.950

MPa 25 MPa 35

% 1000 MPa 1200

J/m 400 °C 123

Minimum order quantity: 5000 Kg

POLYETHYLENE

HE3461
BLACK HIGH DENSITY FOR NON-PRESSURE PIPE APPLICATIONS

DESCRIPTION

HE3461 is a black high density polyethylene for non-pressure pipe application.
The combination of high mechanical strength and long term performance makes HE3461 a suitable material for non-pressure pipe applications.

APPLICATIONS

HE3461 is suitable for non-pressure pipe applications such as non-pressure extruded pipes and cable conduits. HE3461 is not suitable for pressure pipe applications

PHYSICAL PROPERTIES

Property

Density (Compound)
Melt Flow Rate (190°C/5.0kg) Oxidation Induction Time (210°C)

*Data should not be used for specification work

PROCESSING GUIDELINES

Typical Value*

960kg/m3 0.4g/10min ≥15mins

Test Method

ISO 1183 ISO 1133 ISO 11357-6

The actual extrusion conditions will depend on the type of equipment used in addition to the size and wall thickness of the pipe produced. The following conditions may be used as a guideline when starting up the extruder.

Cylinder 170 - 200°C Head 190 - 200°C Die 180 - 190°C

For normal extrusion conditions and applications we suggest preheating and drying with a maximum preheating temperature of 90°C for at least 1 hour.

Specific recommendations for processing conditions can be determined only when the application and type of equipment are known. Please contact your local Borouge representative for such particulars.

STORAGE

The product should be stored in dry conditions at temperatures below 60°C and protected from UV-light. Improper storage can initiate degradation.

Minimum order quantity: 5000 Kg

Marlex® HHM 5502BN HIGH DENSITY POLYETHYLENE This high molecular weight, hexene copolymer is tailored for lightweight blow molded containers that:
 Require excellent stiffness  Require exceptional processability  Are durable and recyclable for sustainability Typical blow molded applications for HHM 5502BN include:  Ice chests and coolers  Household and industrial chemical containers  Food packaging  Pharmaceuticals


This resin meets these specifications:
 ASTM D4976 - PE 235  FDA 21 CFR 177.1520(c) 3.2a, use conditions B through H per 21 CFR 176.170(c) Listed in the Drug Master

• Density: 0.955 g/cm3
• Melt Index: 0.35 g/10 min

Minimum order quantity: 5000 Kg

SABIC® HDPE B1254

HIGH DENSITY POLYETHYLENE

DESCRIPTION

B1254 is a High Density Polyethylene specially developed for blow molding and jerry cans. The material offers good processability and excellent combination of stiffness/ESCR.

TYPICAL APPLICATIONS

B1254 is specially designed for standard jerry cans for packaging of dangerous goods, food /non-food products. This product is not intended for and must not be used in any pharmaceutical/medical applications.